發(fā)布時(shí)間：2018-06-21 23:41

  本文選題：管材腐蝕 + 再生水��； 參考：《腐蝕科學(xué)與防護(hù)技術(shù)》2017年05期

【摘要】：利用水質(zhì)穩(wěn)定性指標(biāo)對再生水廠出水進(jìn)行腐蝕性評價(jià),并選取堿度、硬度、Cl~-和SO_4~(2-)4種因素設(shè)計(jì)四因素三水平正交試驗(yàn),結(jié)合SEM等微觀形貌分析手段,研究高品質(zhì)再生水管網(wǎng)中水泥砂漿內(nèi)襯腐蝕情況及影響水質(zhì)主要因素的綜合作用。結(jié)果表明:該再生水廠高品質(zhì)出水水質(zhì)對水泥砂漿內(nèi)襯具有腐蝕傾向;4種因素對水泥砂漿內(nèi)襯腐蝕影響的主次順序?yàn)?硬度Cl-堿度SO42-;顯著性為:硬度和Cl~-影響較顯著,堿度雖不顯著但有影響,SO_4~(2-)則未對水泥砂漿內(nèi)襯腐蝕表現(xiàn)出顯著影響。此外,高堿度(HCO_3~-)且低硬度時(shí)腐蝕現(xiàn)象最嚴(yán)重。
[Abstract]:Using the water quality stability index to evaluate the corrosion of the effluent from the reclaimed water plant, four factors, such as alkalinity, hardness, Cln- and SO4-, were selected to design four factors and three levels orthogonal test, combined with SEM and other micro-morphology analysis means. The corrosion of cement mortar lining in high quality regenerative water pipe network and the comprehensive effect of main factors affecting water quality are studied. The results show that the quality of high quality effluent from this reclaimed water plant has corrosion tendency to cement mortar lining. The main and secondary factors affecting cement mortar lining corrosion are as follows: hardness Cl-alkalinity so _ 42-, and the significant effects are: hardness and Cl-n-. Although alkalinity is not significant, so _ 4 ~ (2-) has no significant effect on the corrosion of cement mortar lining. In addition, high alkalinity (HCOS3 -) and low hardness corrosion is the most serious.
【作者單位】： 天津大學(xué)環(huán)境科學(xué)與工程學(xué)院;中國市政工程華北設(shè)計(jì)研究總院有限公司;
【基金】：國家自然科學(xué)基金(51478307) 高等學(xué)校博士學(xué)科點(diǎn)專項(xiàng)科研基金(20130032110032)~~
【分類號】：TB304

【相似文獻(xiàn)】

相關(guān)期刊論文 前1條

1 周美英,周建方,劉翠紅;碳纖維/水泥砂漿力學(xué)性能試驗(yàn)分析[J];河海大學(xué)常州分校學(xué)報(bào);2003年04期

相關(guān)碩士學(xué)位論文 前2條

1 鄭楠;環(huán)境侵蝕下水泥砂漿力學(xué)性能的試驗(yàn)研究[D];沈陽工業(yè)大學(xué);2008年

2 楊相璽;聚合物改性水泥砂漿的應(yīng)用基礎(chǔ)研究[D];福州大學(xué);2006年

，

本文編號：2050547