【摘要】：設(shè)計(jì)了自蔓延光固化樹脂體系,并以此為基體制備了UV光固化碳纖維布增強(qiáng)的復(fù)合材料。研究了不同組成樹脂的自蔓延光固化行為。結(jié)果表明,光引發(fā)劑和熱引發(fā)劑相互配合使用可以實(shí)現(xiàn)環(huán)氧樹脂的自蔓延光固化,其中熱引發(fā)劑可以是自由基也可以是陽離子引發(fā)劑,陽離子引發(fā)劑比自由基引發(fā)劑更容易誘發(fā)自蔓延固化。以自蔓延光固化樹脂為基體制備的碳纖維布增強(qiáng)的復(fù)合材料可以實(shí)現(xiàn)快速光固化,其固化過程是樹脂的二維平面自蔓延過程。
[Abstract]:The self-propagating light curing resin system was designed and UV-cured carbon fiber reinforced composites were prepared. The self-propagating light curing behavior of resin with different composition was studied. The results show that the self-propagating photocuring of epoxy resin can be realized by the combination of photoinitiator and thermal initiator, in which the thermal initiator can be free radical or cationic initiator. Cationic initiators are more likely to induce self-propagating curing than free radical initiators. Carbon fiber reinforced composites based on self-propagating light-cured resin can achieve rapid light curing. The curing process is a two-dimensional plane self-propagating process of the resin.
【作者單位】： 海軍航空大學(xué)青島校區(qū)航空機(jī)械系;
【分類號(hào)】：TB332;TQ323.5

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 旱瀨修二;孫勤良;;環(huán)氧樹脂的陽離子光固化[J];熱固性樹脂;1987年04期

2 王德中;;耐熱性光固化型樹脂[J];熱固性樹脂;1990年03期

3 蘭;;高精度光造形裝置及光固化樹脂[J];國外塑料;1992年04期

4 歐亞;;光固化粘合劑[J];粘接;1988年02期

5 萬小龍;;光固化樹脂體系及其應(yīng)用[J];黎明化工;1994年01期

6 張瑾璐,曹瑞軍,王素琴;一種新的光固化樹脂齊聚物合成用催化劑[J];西安交通大學(xué)學(xué)報(bào);2001年06期

7 孫小英;立體光造型法用光固化樹脂的研究述評(píng)[J];浙江科技學(xué)院學(xué)報(bào);2002年04期

8 王素琴,曹瑞軍,段玉崗;光固化樹脂的制備及應(yīng)用[J];化學(xué)工程;1999年06期

9 馬滿珍,蘇孝榮,張秋禹;M9l4阻燃光固化樹脂體系研究[J];玻璃鋼/復(fù)合材料;1992年03期

10 劉丹丹;王欣;劉甜;于潔;郭文勇;;快速成型光固化樹脂的制備[J];工程塑料應(yīng)用;2014年04期

相關(guān)會(huì)議論文 前1條

1 呂波;;我國單體和低聚物現(xiàn)狀及發(fā)展趨勢[A];第九屆中國輻射固化年會(huì)論文集[C];2008年

相關(guān)碩士學(xué)位論文 前3條

1 譚湘璐;桐油在水性光固化樹脂和水性聚氨酯樹脂的應(yīng)用研究[D];湖南大學(xué);2016年

2 劉文龍;改性大豆油光固化樹脂制備研究[D];湖北大學(xué);2016年

3 陳小文;快速成型光固化樹脂體系的研究[D];華南理工大學(xué);2011年

，

本文編號(hào)：2059816